Description:
Lotrène® FD0274 is mainly recommended for the extrusien of thin film for light and medium duty applicaticng. It contains both slip additives(target 600 ppm erucamide) and anti blocking additives (target 900 ppm) as well as antioxidants.
The molecular structure of Lotrène FD0274 is mainly recommended for the extrusien of thin film for light and medium duty applicaticng.
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Melt Flow Index | 2.4 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm³ | ASTM D1505- |
Crystalline Melting Point | 108 | °C | ASTM E794- |
Vicat Softening Point | 89 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
---|---|---|---|
Tensile Strength @ Yield MD/TD | 11 月 11 日 | MPa | ASTM D882- |
Tensile Strength @ Break MD/TD | 24/22 | MPa | ASTM D88- |
Elongation @ Break MD/ TD | 300/600 | % | ASTM D882- |
Impact Strength, F 50 | 110 | g | ASTM D1709- |
Tear resistance MD/ TD | 65/35 | N/mm | ASTM D- 1922 |
Puncture Force | 30 | N | Internal Method |
Haze | 8 | % | ASTM D1003- |
Gloss @ °45 | 59 | ASTM D2457 | -- |
Lotrène® FD0274 can be easlly processed on all types of extuders to make blown or cast films.
The melt temperature is suggested to be in the range of 150-140 °C.
The best propertes of the blown film are achieved at blow up ratlos between 2:1 and 3:1.
To avoid blocking and shrinkage on the reel, temperature at the nip rolls and take-off should be kept as close as possible to the ambient temperature.
The recommended thickness range is from 20 µm to 100 µm.
Polyethylene products should be stored in their original packaging or in clean appropriate silos.
The products should be stored in a dry and well-ventilated area and should not be exposed to direct sunlight and/ or heat in any form since this may adversely affect their properties.
As a general rule, our products should not be stored for more than three months from receipt date.
Under normal conditions Lotrène® products do not present a toxic hazard through skin contact or inhalation. For detailed information please refer to the Safety Data Sheet.
Lotrène® polyethylene products manufactured by Qatar Petrochemical Company (QAPCO) Q.S.C. comply with US, EU and other food contact legislations. Limitations may apply.
All QAPCO Lotrène products are complying with REACH Regulation 1907/2006/EC. The aims of this regulation are to imprave the protection of human health and the environment through better and earlier identificatian of the intrinsic properties of chemical substances.
Please cortact your Muntajat representative for detailed compliance aertficates.
NOT SUITABLE FOR PHARMACEUTICAL OR MEDICAL APPLICATIONS.
The values reported in this technical data sheet are the results of tests carried out in accordance with standard test procedures in a laboratory environment. Actual properties may vary depending on batch and extrusion conditions.
Therefore, the values should nat be used for specificatian puposes.
Before using this product, the user is advised and cautioned to make its own determination and assessment of the safely and suiiability of the produd for the specific use in question, and is further advised against relying on theinformation contained herein as it may relate to any specific use ar application.
It is the ultimate responsibility of the user to ensure that the product is suitable for, and the information is applicable to, the users specific applicatian. QAPCO does not make, and epressly disclaims, all warranties, includinswarranties of merchantability ar fitneas for a particular purpese, regardless of whether aral or writen, expressed or implied, or allegedly arising from any usage of any trade or from any course of dealing, in connection with the use of the information contained herein or the product itself.
The user expressly assumes all risks and liabilities, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Trademarks may not be used in any manner other than expressly authorized in a written agreement and no trademark or license rights of any kind are granted hereunder, by implication or otherwise.